Product Introduction
*High strength, high fluidity, high temperature performance,suitable for unshaped refractory formed by casting
*Materials Carefully chosen, adhere to quality the first and service to the world
*Price compared with peers,with high cost performance,we can meet high demand customers
*Good liquidity,So it is widely used in amorphous refractory materials,material and binder can be selected according to the conditions of use
Specification |
Value |
|
Chemical composition % |
Al2O3 |
70 |
SiO₂ |
20 |
|
SiC |
5 |
|
CaO |
0.8 |
|
Cold compressive strength (Mpa) |
1250℃*3h |
20 |
Cold Bending Strength (Mpa) |
1250℃*3h |
10 |
Heating linear shrinkage % |
1250℃*3h |
±1.2 |
Volume Density |
1250℃*3h |
2.8 |
Added Water % |
5 - 7 |
|
Construction consumption (kg/m3) |
3000 |
Castable material can be delivered in bulk or poured into prefabricated parts for delivery.For castable material delivered in bulk,samples of specified size are usually prepared in the laboratory according to the amount of water added during construction,after curing according to the prescribed curing method, performance test is carried out.For prefabricated parts, samples are usually prepared according to the qualitative product.Unlike qualitative products, refractory castables should normally be measured for their fluidity and burst resistance.Other test items include volume density, flexural and compressive strength, linear rate of change, etc.
http://www.wgfurnace.com/